DISSOLUTION DISCONTINUE DANS L’ALLIAGE Ni-1,4 at. % In DISCONTINUOUS DISSOLUTION IN THE Ni-1,4 at.% In ALLOY
Résumé
L'intérêt particulier de ce travail est la mise en évidence du processus de dissolution discontinue dans l'alliage Ni-1,4 at.%In,
avec l’effet du cycle thermique ainsi que le mouvement inverse du front de réaction, principale caractéristique de cette
réaction. Les techniques d'analyse utilisées à cet égard sont la microscopie optique et la microdurété HV.
The particular interest of this work is the description of the process of discontinuous dissolution in Ni-1,4 at.% In alloy, with
the effect of the thermal cycle as well as the opposite movement of the reaction front, principal characteristic of this reaction.
The techniques of analysis used in this respect are optical microscopy and hardness HV.
Références
[1] W. Gust and R.A. Fouzrnelle, Anais. 7O CBE Cimat,
UFSC, Florianapolis Santa Catarina, p.273-279,
(1986).
[2] P. Zieba and W. Gust, Int. Mater.Rev, p.43, (1998).
[3] I.G. Solarzano and W. Gust, Materials science forum,
vols.94-96, p659-664, (1992)
[4] K.N. Tu and D. Turnbull, Metallurgical Transaction,
Vol.2, p.2511-2515, (1971)
[5] M.S. Sulonen, Acta Metal, Vol.8, p. 1924-1929,
(1960)
[6] H. Chuang, Phd Dissertation, University of Stuttgart,
(1983).
[7] A. Pawlowski and P. Zieba, Mater.Sci.Eng. A.108,
P.9, (1989)
[8] A. Dauger, E.K. Boudili and M. Roth, Scripta Met.,
24, p.1119, (1976).
[9] S. Bensaada, Rev.Met NO2, P.127-133, (2005)
[10] T.H. Chuang, W. Gust and R.A. Fournelle, Eng. And
Sci. of Mat., Universidade Federal, Florianapolis
Santa Catarina, p.7, (1986).
UFSC, Florianapolis Santa Catarina, p.273-279,
(1986).
[2] P. Zieba and W. Gust, Int. Mater.Rev, p.43, (1998).
[3] I.G. Solarzano and W. Gust, Materials science forum,
vols.94-96, p659-664, (1992)
[4] K.N. Tu and D. Turnbull, Metallurgical Transaction,
Vol.2, p.2511-2515, (1971)
[5] M.S. Sulonen, Acta Metal, Vol.8, p. 1924-1929,
(1960)
[6] H. Chuang, Phd Dissertation, University of Stuttgart,
(1983).
[7] A. Pawlowski and P. Zieba, Mater.Sci.Eng. A.108,
P.9, (1989)
[8] A. Dauger, E.K. Boudili and M. Roth, Scripta Met.,
24, p.1119, (1976).
[9] S. Bensaada, Rev.Met NO2, P.127-133, (2005)
[10] T.H. Chuang, W. Gust and R.A. Fournelle, Eng. And
Sci. of Mat., Universidade Federal, Florianapolis
Santa Catarina, p.7, (1986).
Comment citer
BENSAADA, S..
DISSOLUTION DISCONTINUE DANS L’ALLIAGE Ni-1,4 at. % In DISCONTINUOUS DISSOLUTION IN THE Ni-1,4 at.% In ALLOY.
Courrier du Savoir, [S.l.], v. 9, mai 2014.
ISSN 1112-3338.
Disponible à l'adresse : >https://revues.univ-biskra.dz./index.php/cds/article/view/501>. Date de consultation : 14 nov. 2024
Rubrique
Articles